Substrate for optical disc recording media

ABSTRACT

This invention relates to a substrate for optical disc recording media which contains a UV-curable resin film between a transparent film and a thermally-decomposing high molecular film, the UV-curable resin film being formed with a UV-curable resin composition comprising given quantities of: 
     (a) a polybutadiene having acrylic or methacrylic group at one or both ends of the molecule, 
     (b) a hydroxyalkyl acrylate or methacrylate, 
     (c) an acrylic- or methacrylic-group-containing diluent, and 
     (d) a photo-polymerization initiator.

BACKGROUND OF THE INVENTION

This invention relates to a substrate for optical disc recording media which record and reproduce photosignals at a high speed and high density.

DESCRIPTION OF THE PRIOR ART

Optical disc recording media, as illustrated in FIG. 1, are produced by (1) forming, on a transparent substrate 1 made of glass, transparent plastic, etc., a sublayer 2 having a surface unevenness of the form of groove or pit for servotrack, etc., (2) forming, on this sublayer 2, a metal film 3 of Bi, In, Te, As, Pb, Sn, etc. for recording purpose, and then (3) letting two of these structures (1+2+3) thus formed face each other at the metal film side and bonding the transparent substrates 1 to a supporting material (not shown in FIG. 1) with a certain distance maintained between the two structures. Information units are produced by irradiating the metal film 3 for recording purpose with light beams and melting/removing the part of the metal film to form portions where the metal film does not exist. In order to perform the melting/removal of the metal film with a low energy, that is, to improve the sensitivity of recording, the surface of the sublayer 2 is made of a material which is decomposed by the heat of light beams and promotes the melting/removal of the metal film for recording purpose.

Substrates for such optical disc recording media are produced in accordance with steps shown in FIG. 2. That is, they are produced by (a) coating, on a metal stamper 5 made of nickel, etc. and having a given surface uneven pattern, a thermally decomposing, organic, high molecular weight material composed of nitrocellulose, etc. to form a thermally-decomposing high molecular weight film 2-1, (b) placing, between the film and a transparent substrate 1, a UV (ultra violet light)-curable resin 2-2, (c) UV curing the resin to form a sublayer 2, and then (d) detaching the metal stamper 5.

The above-mentioned UV-curable resin is required to meet the following conditions (i) to (iv).

(i) The UV-curable resin, when UV cured, is optically transparent.

(ii) The resin adheres firmly to the transparent substrate composed of glass, transparent plastic. etc.

(iii) The resin does not dissolve the thermally-decomposing, high molecular weight film of nitrocellulose, etc. Also, it does not infiltrate into the film to hinder the separation of the stamper from the film. Further, when UV cured, it adheres well to the thermally-decomposing, high molecular film.

(iv) The resin, when UV cured, does not generate any substance which will corrode the metal film for recording purpose.

Conventional UV-curable resins, however, only partly meet the above conditions (i) to (iv). [Japanese Patent Publication No. 8856/1977, Japanese Patent Application Kokai (Laid-open) No. 86756/1978]

SUMMARY OF THE INVENTION

The object of this invention is to provide a substrate for optical disc recording media free from the drawbacks of the conventional art, by adopting, as the UV-curable resin film placed between the thermally-decomposing high molecular film and the transparent substrate, a film which (i), is optically transparent, (ii), firmly bonds the transparent substrate and the thermally-decomposing, high molecular weight film, (iii), does not infiltrate into the thermally-decomposing, high molecular weight film to hinder the separation of the stamper from the latter film, and (iv), when UV cured, does not generate any substance which corrodes the recording film.

The above-mentioned object of this invention can be achieved by forming the UV-curable resin film between the thermally-decomposing high molecular film and the transparent substrate with a UV-curable resin composition comprising:

(a) a high molecular weight substance of 500 to 10,000 M.W. having acrylic or methacrylic group at one or both ends of the molecule and also a polybutadiene skeleton within the molecule,

(b) at least one compound selected from the compounds represented by the general formulas (1) and (2): ##STR1## wherein R is H or CH₃ and n is an integer of from 2 to 16,

(c) a reactive diluent containing at least one acrylic or methacrylic group within the molecule and having a viscosity of 100 mPa.s or lower at 25° C., (a), (b) and (c) being mixed so as to fall within an area formed by connecting the following three points A, B and C in a triangle,

    ______________________________________                                                        At least one com-                                                              pound selected                                                  The high molecular                                                                            from the compounds                                              substance of 500                                                                              represented by the                                                                            The diluent                                      to 10,000 M.W. above general  mentioned in                                     mentioned in (a)                                                                              formulas (1) and                                                                              (c) above, %                                     above, % by weight                                                                            (2), % by weight                                                                              by weight                                        ______________________________________                                         A   70             30             0                                            B   20             80             0                                            C   20             30             50                                           ______________________________________                                    

and, (d) 0.5 to 5 parts by weight of a photo-polymerization initiator based on 100 parts by weight of a mixture of the above components (a), (b) and (c).

Next, further explanations will be made on these components (a), (b), (c) and (d) used in this invention.

The component (a) imparts moisture resistance, toughness and transparency to the UV-curable resin film, and does not dissolve the transparent substrate when the substrate is made of plastic.

Specific examples of the component (a) include a compound of about 1000 or about 2000 M.W. produced by reacting 1 mole of a poly-1,2-butadiene having hydroxyl group at both ends with 2 moles of tolylenediisocyanate and thereafter reacting an excess of isocyanate group with 2 moles of acrylic acid; a compound of about 1000 or about 2000 M.W. produced by reacting 1 mole of a poly-1,2-butadiene having hydroxyl group at both ends with 2 moles of tolylenediisocyanate and thereafter reacting an excess of isocyanate group with 2 moles of methacrylic acid; and a compound of about 1000 or about 3400 M.W. produced by reacting 1 mole of a butadieneacrylonitrile copolymer having carboxyl group at both ends (acrylonitrile content: 18% by weight) with 2 moles of glycidyl methacrylate. These compounds are used singly or as a mixture of two or more.

When the component (a) has a molecular weight lower than 500, it dissolves the plastic adherend and also reduces the mechanical strength of the cured UV-curable resin composition. When the component (a) has a molecular weight higher than 10,000, the UV-curable resin composition has a high viscosity resulting in reduced work efficiency and therefore such a high molecule can not be used.

The acrylic or methacrylic group at one or both ends of the molecule of the component (a), upon exposure to light, causes a crosslinking reaction immediately to form an optically transparent cured product.

Polybutadiene type high molecular weight substances not having acrylic or methacrylic group at both ends of their molecules are slow-reacting or not reactive causing the insufficient curing or white turbidity of the UV-curable resin composition, and accordingly can not be used as the component (a).

As specific examples of the component (b), there may be mentioned 2-ethyl-2-hydroxyethyl acrylate, 2-ethyl-2-hydroxyethyl methacrylate, 1-ethyl-2-hydroxyethyl acrylate, 1-ethyl-2-hydroxyethyl methacrylate, 2-n-propyl-2-hydroxyethyl acrylate, 2-n-propyl-hydroxyethyl methacrylate, 1-n-propyl-2-hydroxyethyl acrylate, 1-n-propyl-2-hydroxyethyl methacrylate, 2-n-butyl-2-hydroxyethyl acrylate, 2-n-butyl-2-hydroxyethyl methacrylate, 1-n-butyl-2-hydroxyethyl acrylate, 1-n-butyl-2-hydroxyethyl methacrylate, 2-n-pentyl-2-hydroxyethyl acrylate, 2-n-pentyl-2-hydroxyethyl methacrylate, 1-n-pentyl-2-hydroxyethyl acrylate, 1-n-pentyl-2-hydroxyethyl methacrylate, 2-n-hexyl-2-hydroxyethyl acrylate, 2-n-hexyl-2-hydroxyethyl methacrylate, 1-n-hexyl-2-hydroxyethyl acrylate, 1-n-hexyl-2-hydroxyethyl methacrylate, 2-n-decyl-2-hydroxyethyl acrylate, 2-n-decyl-2-hydroxyethyl methacrylate, 1-n-decyl-2-hydroxyethyl acrylate, 1-n-decyl-2-hyroxyethyl methacrylate, 2-n-tetradecyl-2-hydroxyethyl acrylate, 2-n-tetradecyl-2-hydroxyethyl methacrylate, 1-n-tetradecyl-2-hydroxyethyl acrylate, 1-n-tetradecyl-2-hydroxyethyl methacrylate, 2-n-hexadecyl-2-hydroxyethyl acrylate, 2-n-hexadecyl-2-hydroxyethyl methacrylate, 1-n-hexadecyl-2-hydroxyethyl acrylate, 1-n-hexadecyl-2-hydroxyethyl methacrylate, etc. These compounds are used singly or as a mixture of two or more. All these compounds have the effect of imparting adhesivity to the UV-curable resin composition. Also, they have extra-ordinarily good compatibility with polybutadiene type high molecular substances and cause neither phase separation nor turbidity. When the transparent substrate is a 2-hydroxyethyl methacrylate plastic, the compounds of the component (b) do not dissolve and impair the substrate. Accordingly, even if a polymethyl methacrylate or nitrocellulose is used for the transparent substrate, it is not dissolved by the component (b).

When n of the above general formulas (1) and (2) is greater than 16, the UV-curable resin composition has an excessively high viscosity or takes a form of crystal. When n is smaller than 2, the composition can not be used practically.

As the component (c), there may be specifically mentioned lauryl acrylate, lauryl methacrylate, tridecyl methacrylate, isobornyl acrylate, isobornyl methacrylate, neopentyl glycol diacrylate, neopentyl glycol dimethacrylate, trimethylolethane triacrylate, trimethylolethane trimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate, etc. These compounds are used singly or as a mixture of two or more.

All these compounds have a viscosity of 100 mPa.s or lower at 25° C., have good compatibility with the components (a) and (b), and do not dissolve and impair the plastic adherend. When the component (c) has a viscosity higher than 100 mPa.s at 25° C., the UV-curable resin has an increased viscosity and can not be used practically.

As the component (d), there may be used, for example, benzils such as benzil, methyl-0-benzoate and the like; benzoins such as benzoin, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether and the like; benzophenones such as benzophenone, 4-methoxybenzophenone and the like; acetophenones such as acetophenone, 2,2-diethoxyacetophenone and the like; thioxanthones such as 2-chlorothioxanthone, 2-methylthioxanthone and the like; anthraquinones such as 2-ethylanthraquinone, 2-methylanthraquinone and the like; benzyl dimethyl ketal; phenyl ketones such as 1-hydroxycyclohexyl phenyl ketone, 2-hydroxy-2-methyl-1-phenylpropane-1-on, 1-(4-isopropylphenyl)-2-hydroxy-2-methylpropane-1-on and the like; etc. These compounds are used singly or as a mixture of two or more.

In order to further stabilize the adhesion characteristics of the UV-curable resin composition when the composition has absorbed moisture, there may be added a silane coupling agent to the composition. Specific examples of this coupling agent include α-acryloxypropyl trimethoxy silane, α-methacryloxypropyl trimethoxy silane, vinyl trimethoxy silane, vinyl triethoxy silane, N-β-(N-vinylbenzylamino) ethyl-α-aminopropyl trimethoxy silane monohalogen chloride, etc. These compounds are used singly or as a mixture of two or more.

Desirably, the silane coupling agent is added to the UV-curable resin composition in a proportion of 6% by weight or less based on 94% by weight or more of the UV-curable resin composition consisting of the components (a), (b) and (d) or (a), (b), (c) and (d).

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a sectional view of a optical disc recording medium.

FIG. 2 is a drawings illustrating a process for producing a substrate for optical disc recording media.

FIG. 3 is a drawing showing a composition area of a UV-curable resin composition used in the substrate for optical disc recording media of this invention.

FIG. 4 is a graphs showing viscosities and adhesion strengths toward glass, of UV-curable resin composition used in the substrate for optical disc recording media of this invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Hereinunder, this invention will be illustrated in detail referring to Examples.

EXAMPLE 1

As the component (a), there was selected a commercial poly-1,2-butadiene having methacryl group at both ends of the molecule (M.W.: about 2000, brand name: TE 2000, manufacturer: Nihon Soda) produced by reacting 1 mole of a poly-1,2-butadiene having hydroxyl group at both ends of the molecule with 2 moles of tolylenediisocyanate and thereafter reacting an excess of isocyanate group with 2 moles of methacrylic acid. This compound was mixed with equal weight mixtures of two compounds represented by the general formulas (1) and (2) as the component (b) to evaluate their compatibilities. Results were obtained as shown in Table 1.

When n of the general formulas (1) and (2) of the component (b) is equal to or larger than 2, the component (a) and the component (b) are compatible completely and, even if they are allowed to stand in the air to absorb moisture, no turbidity due to partial separation is caused at all. This trend is observed in various mixing proportions of the components (a) and (b). When n of the component (b) is in the range of 2 to 16, mixtures of the components (a) and (b) are extremely stable. Incidentally, to these mixtures of the components (a) and (b) was added 2% by weight of benzoin isopropyl ether as a photo-polymerization initiator of the component (d), and their compatibilities were similar to those in Table 1.

                                      TABLE 1                                      __________________________________________________________________________                                    Component (b)/[Component (a) +                                                 Component (b)],                                                                % by weight                                     Component (a)                                                                             Component (b)       20  40  60  80                                  __________________________________________________________________________     Compound produced                                                                         Equal weight mixture of                                             by reacting 1 mole of  a poly-1,2-butadiene having hydroxyl group at both      ends of the molecule with 2 moles of tolylenediiso- cyanate and                            ##STR2##           Turbid                                                                             Turbid                                                                             Phase separa- tion                                                                 Phase separa- tion                  after reacting an excess of iso- cyanate group with 2 moles of metha-          crylic acid                                                                                ##STR3##            Turbid                                                                             Turbid                                                                             Turbid                                                                             Turbid                                         ##STR4##            Com- patible                                                                       Com- patible                                                                       Com- patible                                                                       Com- patible                                   ##STR5##            Com- patible                                                                       Com- patible                                                                       Com- patible                                                                       Com- patible                       __________________________________________________________________________

EXAMPLE 2

Nitrocellulose (M.W.: 200,000, nitrogen: 11% by weight) was dissolved in n-butyl acetate to obtain a solution containing 1.5% by weight of the former. This solution was spinner-coated on a nickel stamper and dried. The nitrocellulose film thus formed on the nickel stamper had a thickness of about 2 μm.

Separately, in a manner similar to Example 1, the component (a), the component (b) and mixtures of the components (a) and (b) were prepared as shown in Table 2. They were dropped on the nitrocellulose film prepared above. After 30 min of standing at 25° C., the solubility of the nitrocellulose film was examined. As a result, it was confirmed that, in the range of n of 2 to 16, there is a range of the mixing proportion of the components (a) and (b) wherein nitrocellulose is not dissolved.

                                      TABLE 2                                      __________________________________________________________________________                                     Component (b)/[Component (a) + Component                                       (b)],                                                                          % by weight                                    Component (a)                                                                              Component (b)       0    20   40   60   80   100                   __________________________________________________________________________     Compound produced by                                                                       Equal weight mixture of                                            reacting 1 mole of a poly-1,2-butadiene having hydroxyl group at both          ends of the molecule with 2 moles of tolylenediiso- cyanate and                             ##STR6##           In- soluble                                                                         Soluble                                                                             Soluble                                                                             Soluble                                                                             Soluble                                                                             Soluble               after reacting an excess of iso- cyanate group with 2 moles of metha-          crylic acid.                                                                                ##STR7##                 Slight- ly soluble                                                                  Soluble                                                                             Soluble                                                                             Soluble                                ##STR8##                 In soluble                                                                          In- soluble                                                                         In soluble                                                                          In- soluble                                                                         Slight- ly                                                                    soluble                            ##STR9##                 In- soluble                                                                         In- soluble                                                                         In- soluble                                                                         In- soluble                                                                         In- soluble          __________________________________________________________________________

EXAMPLE 3

There were prepared various compositions each consisting of a commercial poly-1,2-butadiene having methacrylic group at both ends of the molecule (M.W.: about 2000, brand name: TE 2000, manufacturer: Nihon Soda) as the component (a) and an equal weight mixture of 2-ethyl-2-hydroxyethyl methacrylate and 1-ethyl-2-hydroxyethyl methacrylate as the component (b). To each composition prepared above, there were added 2% by weight of benzyl dimethyl ketal as a photo-polymerization initiator, namely the component (d), and 2% by weight of vinyl triethoxy silane as a silane coupling agent.

In FIG. 4, there were shown viscosities at 25° C. and adhesive strengths toward a glass plate, of the above-prepared UV-curable resin compositions. The adhesive strengths in FIG. 4 are initial values and these values remained almost same even after standing for 100 hr at 80° C. and 95% RH.

Since good workability is required in production of substrates for optical disc recording media, it is desirable that the above resin compositions have a viscosity of 5×10³ mPa.s or lower at 25° C. Also, to guarantee and reliability of produced substrates, it is desirable that the resin compositions have an adhesive strength toward a glass substrate of 6 MPa or higher. The optimum mixing range of the components (a) and (b) satisfying these conditions is 30 to 80% by weight in terms of % by weight of the component (b) based on the mixture of the components (a) and (b).

EXAMPLE 4

In Table 3, there were shown characteristic properties of composition Nos. 1 to 13 as Example and composition Nos. 14 to 18 as Comparative Example. In these compositions, there were used 1-hydroxycyclohexyl phenyl ketone is a photo-polymerization initiator and α-methacryloxypropyl trimethoxy silane as a silane coupling agent.

As obvious from Table 3, composition Nos. 1 to 13 of this Example do not dissolve a nitrocellulose film, have viscosities lower than 5×10³ mPa.s at 25° C. and possess adhesive strengths (toward glass plate) greater than 6 MPa, and satisfy the target values. On the other hand, composition Nos. 14 to 18 as Comparative Example do not meet the target values partly or wholly.

Mixing proportions of the components (a), (b) and (c) in composition Nos. 1 to 13 of this Example are within the composition area formed by the vertexes A, B and C in triangle as shown in FIG. 3.

When the component (a) in the mixture of the components (a), (b) and (c) is less than 20% by weight, as shown in composition No. 15 as Comparative Example, the composition dissolved the nitrocellulose film. When the component (b) in the mixture of the components (a), (b) and (c) is less than 30% by weight, as shown in composition No. 14 as Comparative Example, the composition had an adhesive strength (toward glass plate) lower than 6 MPa (target value).

    TABLE 3       Example 4 Comparative Example Composition No. 1 2 3 4 5 6 7 8 9 10 11      12 13 14 15 16 17 18        Components, (a) Poly-1,2-butadiene having methacrylic 25 35 55 35 35   3      5 35 35 35 35 20 35 10    parts by  group at both ends (M.W.: about      2000) weight  Poly-1,2-butadiene having acrylic      35   group at both      ends (M.W.: about 1000)   Polybutadiene-acrylonitrile polymer       35      having acrylic group at both ends   (M.W.: about 3400, acrylonitrile      content: 18% by weight)  (b) Equal weight mixture of 2-ethyl-2- 75 65 45        65 65 55 55 55 45 30 30 15 45  65   hydroxyethyl methacrylate and 1-      ethyl-2-hydroxyethyl methacrylate   Equal weight mixture of 2-n-butyl-       65   2-hydroxyethyl methacrylate and 1-n-   butyl-2-hydroxyethyl      methacrylate   Equal weight mixture of 2-n-hexyl-     65             65       2-hydroxyethyl acrylate and 2-n-   hexyl-2-hydroxyethylacrylate  (c)      Tridecyl methacrylate        10  Gen- Neopentyl glycol diacrylate        10 10 35 50 50 45  eral Trimethylolpropane dimethacrylate         10      10  mono- 2-Hydroxyethyl methacrylate                65  mers Bisphenol      A diglycidyl ether diacrylate                35 35 35  (d) Photo-polymeri      zation initiator 2 2 2 2 2 2 2 2 2 2 2 2 2 2 2 2 2 2  Other Silane      coupling agent 2 2 2 2 2  2 2 2 2 2 2 2 2 2 2 2 2 Characteristic      Solubility of nitrocellulose in ← ← ← ← ←      ← ← Insoluble → → → In- Soluble Soluble      Slightly Com- properties composition            soluble   soluble      ponents  Viscosity, mPa.s, 25° C. 130 320 1800 150 370 250 1000      230 400 300 350 290 70 280 30 80 100 caused Adhesive strength Initial      value 7.0 7.7 7.2 7.5 7.0 8.0 8.1 7.8 8.0 8.0 8.0 7.9 7.9 3.0 6.0 4.0      3.0 phase toward glass, After standing 6.9 7.6 7.3 7.3 6.9 7.8 8.0 7.6      7.9 7.9 7.9 7.9 7.8 2.5 5.9 2.5 2.5 separa- MPa, 25° C. for 100      hr at                  tion  80°       C. and 95% RH

EXAMPLE 5

On a nickel stamper having grooves and pits on the surface, there was coated a nitrocellulose solution in n-butyl acetate and dried to form a nitrocellulose film of about 2 μm in thickness. On this nitrocellulose film, there was dropped each of the UV-curable resin composition Nos. 1 to 18 shown in Table 3. On the resin composition, there was further placed a glass plate of 300 mm in diameter and 1.2 mm in thickness. The laminate thus formed was pressed and thereafter exposed to a high pressure mercury lamp to cure the UV-curable resin. Subsequently, the glass plate and the stamper were pulled to opposite directions in order to separate each other. In the laminates using resin composition Nos. 1 to 13 of Example, separation occured between the stamper and the nitrocellulose film, and on the nitrocellulose surface there was precisely transferred the unevenness pattern which had existed on the surface of the stamper. On the nitrocellulose side surface of the nitrocellulose-adhered glass plate, there was formed a Te-based recording film of about 250 Å in thickness by the vapor deposition method. By letting two same laminates thus formed face each other at the recording film side with a distance of about 1 mm maintained and by bonding the peripheral portions of two glass plates with an epoxy resin type adhesive, a optical disc recording medium was produced. These recording media showed excellent information-recording characteristics and no deterioration at all in a continuous life test of over 1000 hr at 60° C. and 95% RH. On the other hand, in the laminates using resin composition Nos. 14 to 18 of Comparative Example, there adhered to the stamper the nitrocellulose and/or the cured, UV-curable resin in separation of the stamper from the glass plate. Thus desired replicas could not be obtained. 

What is claimed is:
 1. A substrate for optical disc recording media which comprises a transparent substrate and a sublayer formed thereon, which sublayer comprises a UV-curable resin film and a thermally decomposing high molecular weight film, characterized in that said UV-curable resin film existing between the transparent substrate and the thermally decomposing high molecular weight film of the sublayer is composed of a UV-curable composition comprising:(a) a high molecular weight substance of 500 to 10,000 M.W. having acrylic or methacrylic group at one or both ends of the molecule and also a polybutadiene skeleton within the molecule, (b) at least one compound selected from the compounds represented by the general formulas (1) and (2): ##STR10## wherein R is H or CH₃ and n is an integer of from 2 to 16, (c) a reactive diluent containing at least one acrylic or methacrylic group within the molecule and having a viscosity of 100 mPa.s or lower at 25° C., (a), (b) and (c) being mixed so as to fall within an area formed by connecting the following three points A, B and C in a triangle,

    ______________________________________                                                        At least one com-                                                              pound selected                                                  The high molecular                                                                            from the compounds                                              substance of 500                                                                              represented by the                                                                            The diluent                                      to 10,000 M.W. above general  mentioned in                                     mentioned in (a)                                                                              formulas (1) and                                                                              (c) above, %                                     above, % by weight                                                                            (2), % by weight                                                                              by weight                                        ______________________________________                                         A   70             30             0                                            B   20             80             0                                            C   20             30             50                                           ______________________________________                                    

and, (d) 0.5 to 5 parts by weight of a photo-polymerization initiator based on 100 parts by weight of a mixture of the above components (a), (b) and (c).
 2. A substrate for optical disc recording media according to claim 1, wherein the high molecular weight substance (a) of 500 to 10,000 M.W. having acrylic or methacrylic group at one or both ends of the molecule and also a polybutadiene skeleton within the molecule is at least one compound selected from the group consisting of a compound produced by reacting 1 mole of a poly-1,2-butadiene having hydroxyl group at both ends with 2 moles of tolylenediisocyanate and thereafter reacting an excess of isocyanate group with 2 moles of acrylic acid; a compound produced by reacting 1 mole of a poly-1,2-butadiene having hydroxyl group at both ends with 2 moles of tolylenediisocyanate and thereafter reacting an excess of isocyanate group with 2 moles of methacrylic acid; and a compound produced by reacting 1 mole of a butadiene-acrylonitrile copolymer having carboxyl group at both ends (acrylonitrile content: 18% by weight) with 2 moles of glycidyl methacrylate.
 3. A substrate for optical disc recording media according to claim 1, wherein the compounds represented by the general formula (1) is at least one compound selected from the group consisting of 2-ethyl-2-hydroxyethyl acrylate, 2-ethyl-2-hydroxyethyl methacrylate, 2-n-propyl-2-hydroxyethyl acrylate, 2-n-propyl-2-hydroxyethyl methacrylate, 2-n-butyl-2-hydroxyethyl acrylate, 2-n-butyl-2-hydroxyethyl methacrylate, 2-n-pentyl-2-hydroxyethyl acrylate, 2-n-pentyl-2-hydroxyethyl methacrylate, 2-n-hexyl-2-hydroxyethyl acrylate, 2-n-hexyl-2-hydroxyethyl methacrylate, 2-n-decyl-2-hydroxyethyl acrylate, 2-n-decyl-2-hydroxyethyl methacrylate, 2-n-tetradecyl-2-hydroxyethyl acrylate, 2-n-tetradecyl-2-hydroxyethyl methacrylate, 2-n-hexadecyl-2-hydroxyethyl acrylate and 2-n-hexadecyl-2-hydroxyethyl methacrylate;the compounds represented by the general formula (2) is at least one compound selected from the group consisting of 1-ethyl-2-hydroxyethyl acrylate, 1-ethyl-2-hydroxyethyl methacrylate, 1-n-propyl-2-hydroxyethyl acrylate, 1-n-propyl-2-hydroxyethyl methacrylate, 1-n-butyl-2-hydroxyethyl acrylate, 1-n-butyl-2-hydroxyethyl methacrylate, 1-n-pentyl-2-hydroxyethyl acrylate, 1-n-pentyl-2-hydroxyethyl methacrylate, 1-n-hexyl-2-hydroxyethyl acrylate, 1-n-hexyl-2-hydroxyethyl methacrylate, 1-n-decyl-2-hydroxyethyl acrylate, 1-n-decyl-2-hydroxyethyl methacrylate, 1-n-tetradecyl-2-hydroxyethyl acrylate, 1-n-tetradecyl-2-hydroxyethyl methacrylate, 1-n-hexadecyl-2-hydroxyethyl acrylate and 1-n-hexadecyl-2-hydroxyethyl methacrylate; the reactive diluent containing at least one acrylic or methacrylic group within the molecule and having a viscosity of 100 mPa.s or lower at 25° C. is at least one compound selected from the group consisting of lauryl acrylate, lauryl methacrylate, tridecyl methacrylate, isobornyl acrylate, isobornyl methacrylate, neopentyl glycol diacrylate, neopentyl glycol dimethacrylate, trimethylolethane triacrylate, trimethylolethane trimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, 1,6-hexanediol diacrylate and 1,6-hexanediol dimethacrylate; and the photo-polymerization initiator is at least one compound selected from the group consisting of benzils, benzoins, benzophenones, acetophenones, thioxanethones, anthraquionones and phenylketones.
 4. A substrate for optical disc recording media according to claim 1, wherein said thermally decomposing high molecular weight film is made of nitrocellulose.
 5. A substrate for optical disc recording media according to claim 1, wherein said UV-curable composition further comprises a silane coupling agent.
 6. A substrate for optical disc recording media according to claim 5, wherein said silane coupling agent is at least one compound selected from the group consisting of α-acryloxypropyl trimethoxy silane, α-methacryloxypropyl trimethoxy silane, vinyl trimethoxysilane, and vinyl triethoxy silane. 